फास्टनर साफ करण्याच्या सहा सामान्य समस्यांचे विश्लेषण

2021-06-18
अधिक चांगल्या प्रकारे वापरण्यासाठीफास्टनर्स, when we use फास्टनर्स, we need regular maintenance, such as regular cleaning of फास्टनर्स, which can improve the efficiency of फास्टनर्स. But when we clean the फास्टनर्स, we often find some problems, mainly there are six common problems.
1. धुण्यादरम्यान निर्माण होणारे प्रदूषण
After the फास्टनर्स were quenched, they were cleaned with silicate cleaning agent and then rinsed. Solid materials appeared on the surface. The infrared spectrometer was used to analyze this material and it was confirmed to be inorganic silicate and iron oxide. This is caused by the incomplete rinsing and residual silicate on the surface of the फास्टनर.

2. चे अवास्तव स्टॅकिंगफास्टनर्स
Fasteners show signs of discoloration after tempering. Use soaking to allow oily residue to remain after volatilization, which is a high content of lipids. It shows that the फास्टनर is contaminated by cleaning agent and quenching oil during the rinsing period, and it melts at the heat treatment temperature, leaving chemical burn scars. Such substances confirm that the surface of the फास्टनर is not clean. Analyzed by infrared spectrometer, it is a mixture of base oil and ether in quenching oil. The ether may come from the addition of quenching oil. The analysis results of the quenching oil in the mesh belt furnace confirmed that the फास्टनर्स are slightly oxidized in the quenching oil due to unreasonable stacking when heating, but it is almost negligible. This phenomenon is related to the cleaning process, not the quenching oil. The problem.


3. पृष्ठभागाचे अवशेष

उच्च-शक्तीच्या स्क्रूवर एक पांढरा अवशेष आहे, ज्याचे इन्फ्रारेड स्पेक्ट्रोमीटरद्वारे विश्लेषण केले गेले आणि फॉस्फाइड असल्याची पुष्टी केली गेली. कोणतीही अम्लीय क्लीनिंग एजंट साफसफाई केली गेली नाही आणि रिन्सिंग टाकीच्या तपासणीत असे दिसून आले की टाकीच्या द्रवमध्ये कार्बन विद्राव्यता जास्त आहे. टाकीचा द्रव नियमितपणे ओतला पाहिजे आणि रिन्सिंग टँकमधील लाईची एकाग्रता पातळी वारंवार तपासली पाहिजे.

4. अल्कली जळते
उच्च-शक्तीचे स्क्रू उष्णता शमन करून काळे केले जातात आणि एकसमान आणि गुळगुळीत तेल-काळा बाह्य पृष्ठभाग असतो. तथापि, बाह्य वर्तुळात नारिंगी XX सह उघड्या डोळ्यांना दृश्यमान क्षेत्र आहे. याव्यतिरिक्त, असे क्षेत्र आहेत जे किंचित हलके निळे किंवा हलके लाल आहेत. कोल्ड हेडिंग आणि टॅपिंग सुलभ करण्यासाठी मूळ बार आणि वायर रॉड फॉस्फेटिंग फिल्मसह लेपित आहेत. ते न धुता थेट उष्णतेवर उपचार केले जातात, शमन तेलात थंड केले जातात, अल्कधर्मी डिटर्जंटने साफ केले जातात, ब्लो-ड्राईड (धुऊन नाहीत), 550 डिग्री सेल्सिअस तपमानावर, गरम टेंपरिंग फर्नेसमधून गंजविरोधी तेल काढून टाकल्यावर, लाल ठिपके दिसतात स्क्रू धागे.
It has been tested that the red area on the screw is caused by alkali burns. The chloride-containing substances and calcium-containing compounds of the alkaline cleaning agent will burn the steel फास्टनर्स during the heat treatment, leaving scars on the surface of the फास्टनर्स.
Iron and steel फास्टनर्स cannot remove surface alkalis in the quenching oil, so that the surface burns in the high-temperature austenite state and aggravates the damage during the next step of tempering. The recommendation is to thoroughly clean and rinse the फास्टनर्स before heat treatment to completely remove the alkaline residues that cause the फास्टनर्स to burn.


5. अयोग्य rinsing

मोठ्या आकारासाठीफास्टनर्स, पॉलिमर जलीय द्रावण सहसा शमन करण्यासाठी वापरले जाते, आणि अल्कधर्मी स्वच्छता एजंट शमन करण्यापूर्वी स्वच्छ आणि स्वच्छ धुण्यासाठी वापरले जाते. शमन केल्यानंतर,फास्टनर्स have rusted on the inside. Analysis with infrared spectrometer confirmed that in addition to iron oxide, there are sodium, potassium and sulfur, indicating that there is an alkaline cleaning agent on the inside of the फास्टनर, which is likely to be potassium hydroxide, sodium carbonate or similar substances, which promotes its rust. Rinse the फास्टनर्स to check whether there is excessive contamination, and it is also recommended to change the rinse water frequently. In addition, adding rust inhibitors to the water is also a good way.

6. अति गंज
काही काळ्या पट्टे सहसा उच्च शक्तीमध्ये दिसतातफास्टनर्स. It has also been seen in the test that the फास्टनर्स before the heat treatment have been rinsed with inorganic and organic cleaning agents. After quenching, there are still black stripes and even careful cleaning before heat treatment. , Will also leave streaks after heat treatment. Infrared spectrometer was used to analyze the residual pollutants on the surface, and it was found that there were higher concentrations of sulfur and calcium. With a small amount of acetic acid and isopropanol, fold a small piece of test filter paper on the dark spot and wipe it firmly, leaving the dark spot on the filter paper. Analysis of the filter paper with infrared spectrometer confirmed that calcium, sulfur, iron, manganese and chromium are the main elements.


गंज स्पॉट्समध्ये कॅल्शियम आणि सल्फरची उपस्थिती दर्शवते की हा पदार्थ एक शमन करणारे तेल आहे जे कोरडे झाले आहे, आणि शमन प्रक्रियेदरम्यान वाष्प टप्प्यांची उत्क्रांती देखील आहे. कारण शमन करणारे तेल अतिवृद्ध आहे, जुने तेल ओतणे, नवीन तेल घालणे आणि संपूर्ण प्रक्रिया चक्र दरम्यान प्रक्रिया देखरेख आणि शमन तेल देखभाल करण्याची शिफारस केली जाते.